Solvent-based pressure sensitive adhesive / 2 Component / Hih tack and excellent stickabiklity at low temperature

Features

Product name			CT-5030
Appearance			Light yellowish viscidity liquid
Viscosity (mPa・s @25℃)			49.0-51.0
Viscosity (mPa・s @25℃)			1,000-4,000
Solvent			Ethyl acetate, Hexane
Hardener			E-2C
Hardener amount (Wet)			0.75
Composition			Single side	Double-sided
Peel strength (Single side) [N/25mm] (Double-sided) [N/20mm]	SUS (Exfoliation)		20 (partlially CF)	29 (CF)
	PP (Exfoliation)		22 (CF)	28 (CF)
Ball tack			12	21<
Probe tack [N/cm²]		23℃	21	25
		10℃	24	29
		0℃	24	34
Holding power	SUS	40℃ 500g	24h<	24h<

Single side

Processing method: Transfer method
Composition: Coating substrate: Release PET Film(50μm)/ Paste substrate: PET Film(25μm)/ Coating amount: 25g/㎡(dry)
Drying condition: 80℃ x 3 minutes
Aging condition: 40℃ x 3days

Double-sided

Processing method: Transfer method
Composition: Coating substrate: Release paper/ Core substrate: Rayon NWF(14g/㎡)/ Coating amount: each 63g/㎡(dry)
Drying condition: 80℃ x 3 minutes
Aging condition: 40℃ x 3days
Backing substrate: PET Film(25μm)

Peel strength:

Adherends: SUS, PP, Test piece (Single side) 25mm width, (Double-sided) 20mm width
Lamination: 2kg roller X 1 back and forth, Aging conditions:23℃, 50%RH X 30min.
Measurement conditions:23℃, 50%RH, Peel angle: 180°, Peel speed:300mm/min.

Holding power:

Adherends: SUS, Lamination size (Single side) 25mm X 25mm, (Double-sided) 20mm X 20mm
Lamination: 2kg roller X 1 back and forth, Aging Conditions:23℃, 50%RH X 30min.
Measurement conditions:70℃, 1kg load, Keep 24hrs or note the time for drop

Probe tack:

Contact speed: 10mm/s, Peel speed: 10mm/s, Contact condition: 0.98N/cm2 Load x 1 sec. hold

Ball tack:

Functional Products