QUICKMASTER SPS-945NT

Features

• Strong adhesion at high temperature, anti-repulsion and constant load peel

• Strong adhesion on polyolefin, various foams and metals

Process conditions

Single side

• Processing method: Transfer method
• Composition: Coating substrate: Release PET Film(50μm)/ Paste substrate: PET Film(25μm)/ Coating amount: 25g/㎡ (dry)
• Drying condition: 80℃ x 3 minutes
• Aging condition: 40℃ x 3days

Double-sided

• Processing method: Transfer method
• Composition: Coating substrate: Release paper/ Core substrate: Rayon NWF(14g/㎡)/ Coating amount: each 63g/㎡(dry)
• Drying condition: 80℃ x 3 minutes
• Aging condition: 40℃ x 3days
• Backing substrate: PET Film(25μm)

Measurement conditions

Peel strength:

• Adherends: SUS, PP, Test piece (Single side) 25mm width, (Double-sided) 20mm width
• Lamination: 2kg roller X 1 back and forth, Aging conditions:23℃, 50%RH X 30min.
• Measurement conditions:23℃, 50%RH, Peel angle: 180°, Peel speed:300mm/min.

Holding power:

• Adherends: SUS, Lamination size (Single side) 25mm X 25mm, (Double-sided) 20mm X 20mm
• Lamination: 2kg roller X 1 back and forth, Aging conditions:23℃, 50%RH X 30min.
• Measurement conditions: 70℃, 1kg load, Keep 24hrs or note the time for drop

Constant load holding power:

• Adherends : SUS, PP, Lamination size : 20mm X 50mm
• Measurement conditions: 23℃, 300g load, peel distance after 1h and 3h or note the time for drop

Ball tack:

• J. Dow Method (23℃, 50%RH)