QUICKMASTER CT-6030 & CT-6050
Functional Products
Electronics
Automotive
Packaging
Health Care
Color
Display
House Equipment / Infrastructure
Functional Materials
Solvent-based pressure sensitive adhesive / 2 Component / Strong adhesion with optical transparency
Features
-
Strong adhesion with optical transparency for OCA and Anti-scattering films
-
Strong adhesion on Glass, Polycarbonate and other plastics
-
QUICKMASTER CT-6030
Acid-Free and suitable for touch screen modules which metal erosion is concerned
High optical transparency and strong adhesion
Keep high optical transparency and strong adhesion after heat resistance test -
QUICKMASTER CT-6050
Low initial tack, strong adhesion and high transparency
Keep high optical transparency and strong adhesion after heat and moisture resistance test
Performance
| Product name | CT-6030 (Acid free) |
CT-6050 (Low initial tack) |
||
|---|---|---|---|---|
| Appearance | Light yellowish viscidity liquid | Light yellowish viscidity liquid | ||
| Nonvolatile content (%) | 45.0-47.0 | 39.0-41.0 | ||
| Viscosity (mPa・s @25℃) | 4,000-6,000 | 7,000-18,000 | ||
| Solvent | Ethyl acetate, MEK | Ethyl acetate, MEK | ||
| Hardener | DN | EX-50 | ||
| Hardener amount (Wet) | 1.0 | 0.2 | ||
| Peel strength [N/25mm] |
Glass (Exfoliation) |
19 (AF) |
25 (AF) |
|
| Ball tack | － | ＜2 | ||
| Optical properties |
Haze (H) % | 0.3 | 0.4 | |
| Transparency (Tt) % | 92 | 92 | ||
| Yellowing (b*) | 0.1 | 0.1 | ||
Process conditions
Peel strength/ Ball tack
- Processing method: Transfer method
- Composition: Coating substrate: Release PET Film(50μm)/ Paste substrate: PET Film(50μm)/ Coating amount: 25g/㎡(dry)
- Drying condition: 80℃ x 3 minutes
- Aging condition: 40℃ x 3days
Optical properties
- Composition: Web less
- Coated and laminated substrates: Release PET Film(50μm)/ Coating amount: 50g/㎡(dry)
- Drying condition: 60℃ x 3 minutes + 100℃ x 3min.
- Aging condition: 40℃ x 3days
Measurement conditions
Peel strength:
- Adherend: Glass (surface water contact angle 30±10°)
- Test piece: 25mm width
- Lamination: 2kg roller X 1 back and forth, Aging conditions: 23℃, 50%RH X 30min.
- Measurement conditions:23℃, 50%RH, Peel angle: 180°, Peel speed:300mm/min.
Ball tack:
- J. Dow Method (23℃, 50%RH)
Optical properties (Haze, Transparency and Yellowing):
- Adherends: Glass (surface water contact angle 30±10°)
- Test piece: 25mm width
- Lamination: 50℃, 0.5MPa x 20min
- Measurement conditions: PSA Film + Glass(*)
- *Glass : Haze=0.2%, Transparency=91.8%, Yellowing (b*)=0.1