TYFORCE Product Lineup
Functional Products
Electronics
Automotive
Packaging
Health Care
Color
Display
House Equipment / Infrastructure
Functional Materials
H-845
An adhesive with good handling and low viscosity. It is easy to handle with low viscosity while at the same time possessing high initial bonding strength.
-
Combines low viscosity and high initial bonding strength.
-
Trace amount coatings possible.
-
Good bonding characteristics on various base materials.
| Active components | 100% |
|---|---|
| Melt viscosity | 2,000 to 4,000 mPa·s (@125°C) |
| Open time | 60 to 90 seconds (@23°C) |
FH-100
An adhesive for high speed processing. It is easy to handle with low viscosity while at the same time it has fast reactivity to make bonding work at high speeds possible.
-
Possess suitability for bonding work at high speeds.
-
Excellent initial grip characteristics.
-
Can be reworked immediately after processing.
| Active components | 100% |
|---|---|
| Melt viscosity | 4,000 to 10,000 mPa·s (@125°C) |
| Open time | 30 to 60 seconds (@23°C) |
FH-400
An adhesive that combines high initial strength and a long open time.
-
Quick rise in initial strength.
-
Possess a long open time.
-
Suitable for laminating panels with large areas.
-
Good bonding characteristics on various base materials.
| Active components | 100% |
|---|---|
| Melt viscosity | 25,000 to 40,000 mPa·s (@125°C) |
| Open time | 120 to 300 seconds (@23°C) |
FH-315
An adhesive with a broad range of applicable environment temperatures during processing.
-
Accommodates the on-site environment in summer or winter.
-
Exhibits high initial bonding strength.
-
Good bonding characteristics on various base materials.
| Active components | 100% |
|---|---|
| Melt viscosity | 17,000 to 27,000 mPa·s (@125°C) |
| Open time | 30 to 90 seconds (@23°C) |
HH-100
An adhesive that is easy to handle during processing with excellent weather resistance.
-
Excellent applicator stability, easy to handle.
-
Excellent weather resistance.
-
Excellent discoloration resistance.
-
Capable of obtaining high hardness.
-
Capable of coloring white.
| Active components | 100% |
|---|---|
| Melt viscosity | 7,000 to 15,000 mPa·s (@120°C) |
| Open time | Up to 60 seconds (@20°C) |
HH-600
An adhesive that possess flame retardant.
-
Excellent flame resistance.
-
Halogen free.
-
Excellent hydrolysis resistance.
-
Low viscosity so excellent workability.
| Active components | 100% |
|---|---|
| Melt viscosity | 20,000 to 30,000 mPa·s (@120°C) |
| Open time | Up to 60 seconds (@20°C) |
PN-9
A low cure shrinkage adhesive (for mirrored surface applications). When laminating a mirrored surface, will not damage the surface's mirrored impression.
-
Low percentage of shrinkage after curing.
-
Good leveling when coating.
-
Capable of obtaining high hardness.
-
When laminating sheets or films, will not damage the surface's mirrored impression.
| Active components | 100% |
|---|---|
| Melt viscosity | 10,000 to 15,000 mPa·s (@120°C) |
| Open time | Up to 90 seconds (@35°C) |
Exp.BU-1000
An injection molding adhesive capable of low temperature processing.
-
Excellent low temperature workability.
-
Capable of injection molding using aluminum molds.
-
Rapid onset of curing, can be removed from the mold in tens of seconds after being injected.
-
Exhibits high hardness.
-
Possess flame resistance.
-
Excellent adherence on vinyl chloride.
| Active components | 100% |
|---|---|
| Melt viscosity | 10,000 to 20,000 mPa·s (@120°C) |
| Demold time | 20 seconds (@23°C) |
| Molded product hardness | 98 (JIS A) |
Exp.NB-100
An adhesive that possess moisture resistance.
-
Excellent moisture resistance.
-
High hardness. (90 Shore A)
| Active components | 100% |
|---|---|
| Melt viscosity | 8,000 to 12,000 mPa·s (@120°C) |
| Open time | 90 to 120 seconds (@23°C) |
| Moisture resistance performance | 15 g/m2/24 hours |
NH-320
An adhesive that combines flexibility and durability.
-
The resin possess flexibility after curing.
-
Possess high durability.
-
Capable of being applied at low temperatures (80°C).
| Active components | 100% |
|---|---|
| Melt viscosity | 1,000 to 3,000 mPa·s (@125°C) |
| Open time | 180 to 300 seconds (@23°C) |
WT-004
A hot melt adhesive that possess moisture permeability.
-
Excellent moisture permeability.
-
Can be combined with UV curing.
-
Forms a flexible film.
-
Excellent hydrolysis resistance.
| Active components | 100% |
|---|---|
| Melt viscosity | 2,000 to 7,000 mPa·s (@120°C) |
| Moisture permeability performance | 5,000 (g/m2/24 hours) <A-1 method, 50 μm thick> |
Exp.DC-200
A UV-curable hot melt adhesive.
-
In combination with UV curing, exhibits initial strength, so it has excellent productivity.
-
Excellent quick curability by UV curing.
-
There are also types that have transparency.
-
Excellent durability (hydrolysis resistance/heat resistance).
| Active components | 100% |
|---|---|
| Melt viscosity | 1,000 to 6,000 mPa·s (@120°C) |
| Open time | Adjustable with combined UV use |
Inquiry About This Product
-